Using an innovative procedure known as metal vapor synthesis (MVS) to prepare bimetallic catalysts, starting from Au and Pd vapors, [AuPd] co-evaporated and [Au][Pd] separately evaporated bimetallic catalysts were achieved. After being tested, the catalytic activity and selectivity of the [AuPd] catalyst turned out to be higher than the [Au][Pd] ones. Using EXAFS spectroscopy it was shown that, in the [AuPd] samples, small bimetallic AuPd nanoparticles were present, having an Au rich core surrounded by an AuPd alloyed shell while in the [Au][Pd] sample there was the presence of monometallic Au and Pd nanoparticles showing some alloying only in the boundary regions. The EXAFS results were also qualitatively conrmed by the XANES spectra.
A., B., C., E., E., S., G., V., L., B., Gmartra, ., et al. (2013). EXAFS and XANES structural characterization of bimetallic AuPd vapor derived catalysts. JOURNAL OF PHYSICS. CONFERENCE SERIES, 430, 012052-012055 [10.1088/1742-6596/430/1/012052].
EXAFS and XANES structural characterization of bimetallic AuPd vapor derived catalysts.
MOBILIO, Settimio
2013-01-01
Abstract
Using an innovative procedure known as metal vapor synthesis (MVS) to prepare bimetallic catalysts, starting from Au and Pd vapors, [AuPd] co-evaporated and [Au][Pd] separately evaporated bimetallic catalysts were achieved. After being tested, the catalytic activity and selectivity of the [AuPd] catalyst turned out to be higher than the [Au][Pd] ones. Using EXAFS spectroscopy it was shown that, in the [AuPd] samples, small bimetallic AuPd nanoparticles were present, having an Au rich core surrounded by an AuPd alloyed shell while in the [Au][Pd] sample there was the presence of monometallic Au and Pd nanoparticles showing some alloying only in the boundary regions. The EXAFS results were also qualitatively conrmed by the XANES spectra.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.